Category: Secondary Stainless Steel Show

In engineering and manufacturing, poor steel shape can cause serious structural and functional problems, affecting the performance and reliability of buildings, bridges, machinery and equipment,

Features: When CRM is threading, the linear defects caused by the contact between the threading guide plate and the strip steel generally occur at the head and

Features: The surface is peeling off in a linear shape, some are covered by film, and some are not covered by film, which are large

Features: The surface of the steel coil is peeled off like a mountain without a fixed location. Causes: The slab is accompanied by inclusions, the hot rolling

Hot-rolled stainless steel is a versatile material that is used across a wide range of industries due to its strength, durability, and affordability. However, like

Features: The hot-rolled steel coil has poor coil shape after coiling, and is in the shape of a tower. Causes: 1. The edges of the

In engineering and manufacturing, steel edge cracks are a common but serious problem that can negatively impact the strength and durability of structures and equipment.

Feature: Edge wire and burr of hot rolled edge. Cause: There is a sickle bend in the steel coil, and the edge is in strong

In the manufacturing and construction sectors, steel edge loss is an important issue affecting structural stability and performance. Edge loss can occur due to improper

Features of Cloud Pattern: The surface of the steel coil is peeled off like a mountain without a fixed location. Causes: The slab is accompanied by inclusions,